DIBHALITE - SLF
(Waterbased Epoxy Putty)

INTRODUCTION:

Since building construction activity has gained  enormous  uplift, it  is  known  fact  that  the  whole construction activity has been commercialized. Repercussion of which are drasting and  uncontrollable  One of these is “LEAKAGE” - infect  it  is  a  LEAK- AGE. To  overcome  leakage problems, many conventional methods are prevailing in the market, but  these  treatments have not proved to be result oriented due to which waterproofing still remains a “pressing” problem.

DIBHALITE -SLF,  an semi -liquid flowable Waterbased epoxy system, high solid two components  Epoxy based [i.e. Resins & Hardener]  and loaded with basic fillers & extenders, air drying systems, specially formulated to fill cracks, voids, pin-holes and joints. The various applications in construction industry, are given hereunder.

SAILENT FEATURES:

• It  chemically cures at  30⁰C . and no additional curing method is required.

• Being Waterbased Epoxy, it can be applied  on  damp surfaces   unlike pure Epoxy   resins.

• It is odorless, non-flammable, non-toxic enhance it can even be applied in potable water tanks.

PROMINENT TECHNICAL PROPERTIES :

FIELD OF APPLICATION:

APPLICATION ON BATHROOM/TOILETS:

Join between glazed tiles be filled in with the readymade putty “DIBHALITE -SLF” instead of filling it with cement. The putty shall have an excellent bonding and being epoxy based shall with stand acid washes. Joints of W.C. Pan and ‘Nani Trap’ be coated with putty “DIBHALITE-SLF”.

APPLICATION  ON DOOR /WINDOW/ALUMINUM SECTION:

The gap between the wooden frames (door/windows) or Aluminum section and the cement surface can be bridged with readymade putty “DIBHALITE-SLF”. his will prevent the water penetration to the room.

APPLCATION ON DAMP SURFACES: (Flooring & walls)

We recommend “DP-250” as an primer coat, which being Waterbased Epoxy Resins system shall take care of dampness or moistures presents in the concrete surfaces. For more strength, cracks, even level of surface - Epoxy putty “Dl-SLF” shall be coated with min.2 mm thickness.

APPLICATION TO FILL CRACKS:

Cracks and void developed on terraces/water tanks/building structures can be successfully filled in by applying prime coat of DP-250 in the crack and after two hours the joints/voids can be bridged with DIBHALITE -SLF.

APPLICATION TO TREAT EFFLORESENCES/LATENCES:

1.    Clean the surface with wire brush to remove effloresces and latencies. Wash the entire surface with   
 water and wait till dried. Apply prime coat of DP-250.

2.    On curing of prime coat (after 2 - 3 hrs.) apply 2mm thick putty of DL-SLF and when dried, paint the  
 surface.

APPLICATION ON ASBESTOS SHEET:

On the joints/cracks of asbestos sheet, directly apply DIBHALITE -SLF .Moreover, on the junction (i.e. the asbestos sheet and the building structure) apply one coat of DP -250.On curing of primer apply DIBHALITE -SLF with min.2 mm thickness, which shall fill up the cracks.

PRECAUTION:

Mix only the required quantity of DP-250 and DL-SLF, which can be utilize within stipulated pot-life period to avoid solidification. Wash all tools and tackles with ample of water immediately after application  is completed

WATERPROOFING OF DAMP WALLS BY  DP-250   &   DL-SLF

Dibhapoxy-250 & Dibhalite-SLF is an Waterbased Epoxy Resin system and is two pack components (i.e. Resin and Hardener ), wherein “DP-250 “  is to be treated as primecoat as it has brushable consistency and “DL-SLF “  as putty as loaded with required fillers to stop the dampness of internal walls . Moreover, our technical information’s and recommendations contained here in are based on reliable test and accepted to be ultimate solutions to any raising dampness of masonry surfaces (walls).

1.    Remove the old existing layers of paint to the original  laser surface by chipping  and clean the loose
 particles of sand  & cement and clean the same adequately by plenty of water .

2.    If on plaster the cracks are seen by naked eyes than shape the same in “ V “ shape by proper
       chipping. And the surface should be clean by wire brush followed by  water if required .

3.    Mix “ DP-250 “ both the parts in equal proportions by volume by giving stirring for  2 - 3
 minutes  and apply coat with painting brush . Clean the brush with plenty of  water for further 
 use. Allow the prime coat to cure for minimum 5 - 6 hrs. at 35`C.

4.    On curing of prime coat , mix “DL-SLF “ with equal proportions and apply the same on entire surfaces
 with minimum 1.5 - 2.0 mm thickness. Allow to cure the putty for 3 - 4 hrs at 35`C.

5     On complete curing of the system cited above , normal painting can be carried out.

Here the first coat shall give adequate bond in between Plaster and “DL-SLF “ shall fill up the cavity of small hair cracks alongwith even level of surface. Moreover “DP-250 “ shall cover 50 - 60 sq.ft. per single coat and “DL-SLF “ shall cover 25 - 30 sq.ft. per 1.5 - 2.0 mm thickness.

For furthermore information’s please contact the manufacturers.